Coated airbag

ABSTRACT

A coated airbag is provided. In another aspect, a method of extrusion coating an air impermeable material onto a one-piece woven airbag fabric is employed. Another aspect preheats a fabric such that the fabric remains hot during a coating application thereon. Furthermore, a machine for making and coating an airbag fabric is also provided.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application claims the benefit of U.S. Provisional Application No. 61/145,202, filed on Jan. 16, 2009, which is incorporated by reference herein.

BACKGROUND

The present application pertains generally to coated fabrics and more particularly to coated airbags for automotive vehicles.

Simple cut and sew airbags have been commonly used for front and side passenger protection in automotive vehicles. Many modern side curtain airbags, however, must protect the passengers during a vehicular rollover situation and thereby must retain the inflation gas within the airbag for an elongated period of time. Traditional cut and sew airbags have a relatively simple to manufacture fabric construction but often require expensive coatings applied in a relatively complex manner in order to overcome undesired inflation gas leakage through the sewn seams when used for side rollover airbags. Examples of such traditional coated, cut and sew airbags can be found in U.S. Patent Publication No. 2001/0049243 entitled “Lightweight, High Strength Coated Fabric” invented by Crouch et al., and PCT Patent Publication No. WO 2007/070465 entitled “Thermoplastic Coated, Heat-Sealed Airbag” listing Sescourka et al. as inventors. Both of these patent publications are incorporated by reference herein.

One-piece woven (“OPW”) airbags have also been employed for side curtain airbags. Examples of such OPW airbags can be found in the following U.S. patents and patent publications: U.S. Pat. No. 5,685,347 entitled “Circular Air Bag Made of Two Simultaneously Woven Fabric” which issued to Graham et al. on Nov. 11, 1997; 2005/0161919 entitled “Airbag and Method of Producing an Airbag” invented by Berger et al.; and 2002/0140218 entitled “One-Piece Woven Airbag” invented by Beasley, Jr. These patents and publications are all incorporated by reference herein. A knife-over-roll coating process has been used for some conventional OPW airbags, however, this undesirably allows for considerable thickness variations in the coating and can be a costly process. Furthermore, some conventional OPW airbags have used a laminated film approach as an alternative to the knife-over-roll coating process, but this tends to be undesirably expensive and creates difficult to fold stiffness in the final airbag. It is noteworthy, however, that U.S. Pat. No. 7,179,762 entitled “Motor Vehicle Air Bag and Fabric for Use in Same,” invented by Beasley, Jr., states at the top of column 2 that “it is relatively difficult to coat a one-piece curtain” airbag as compared to simpler cut and sew fabric constructions.

SUMMARY

In accordance with the present invention, a coated airbag is provided. In another aspect, a method of extrusion coating an air impermeable material onto a one-piece woven airbag fabric is employed. Another aspect preheats a fabric such that the fabric remains hot during a coating application thereon. Furthermore, a machine for making and coating an airbag fabric is also provided. In yet another aspect, a vehicular airbag has a one-piece woven construction with an outer coating of high molecular weight, thermoplastic material.

The present coated airbag, machine and methods are advantageous over traditional constructions, machines and processes, since the present airbag employs considerably less expensive coating materials while achieving superior performance. The materials employed for the present coating (and entire airbag) are also recyclable, thereby reducing scrap costs, and the coating is easily applied in a uniformly thick manner that is independent of fabric weaving variations. Additionally, lighter weight coating materials are used in the present system, especially as compared to more expensive silicone materials, but without sacrificing performance. This also allows for a reduced packaging size for the final airbag in the vehicle. Additional advantages and features of the present invention will become apparent from the following description and appended claims, taken in conjunction with the accompanying drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a perspective view showing a coated airbag, in an inflated condition, employed in an automotive vehicle;

FIG. 2 is a diagrammatic perspective view showing the equipment used to make the coated airbag;

FIG. 3 is a diagrammatic cross-sectional view, taken along line 3-3 of FIG. 1, showing an exemplary one-piece woven fabric, prior to coating;

FIG. 4 is a diagrammatic side view showing the equipment used to make the coated airbag; and

FIG. 5 is a diagrammatic cross-sectional view of the airbag, after coating.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT

FIGS. 1, 3 and 5 show an exemplary airbag 11 employed in an automotive vehicle 13. Preferably, this airbag is of a side curtain airbag variety which is suitable for retaining a majority of its inflation gas for at least five seconds from full inflation, to meet suitable vehicular rollover requirements. More particularly, airbag 11 includes a one-piece woven fabric 14, having a single layer seam 15 integrally woven to multiple fabric layers 17 surrounding a gas inflation chamber 19 therebetween. In the exemplary embodiment, both 3×3 woven baskets 21 and 2×2 woven baskets 23 are employed in the single layer seam 15 between the pair of double layer inflation chambers 19.

The OPW fabric fibers are preferably made of nylon 6/6, although it is alternately envisioned that a high tenacity polyester material can be employed. OPW fabric 14 is woven on a programmable jacquard loom 25 (see FIG. 4). Exemplary jacquard looms are disclosed in U.S. Pat. No. 4,440,196 entitled “Double Open-Shed Jacquard Machine for the Lifting of Warp Yarns of a Loom” which issued to Arvai on Apr. 3, 1984, and U.S. Pat. No. 6,945,282 entitled “Method and Device for Forming a Shed in a Weaving Machine” which issued to Gendelman et al. on Sep. 20, 2005; both of which are incorporated by reference herein.

Referring to FIGS. 4 and 5, a coating 31 is located on each outside surface of the fabric portion of airbag 11. Coating 31 includes an inner adhesive material 33, penetrating into and bonded with the fabric fibers, and an outer air impermeable and leak-resistant material 35 bonded to adhesive material 33. Adhesive material 33 is preferably a thermoplastic material such as an ethylene copolymer, exhibiting a molecular weight range that is suitable for molten extrusion. One such adhesive material is the Entira™ Coat 100 material which can be obtained from E.I. du Pont de Nemours and Company, Inc. The preferred air impermeable material is a thermoplastic polyurethane (“TPU”) polymer which has a molecular weight within a range of 100,000-200,000. The ultimate elongation percentage of the preferred air impermeable polymeric material is greater than 300, and more preferably within the range of 500-700. Furthermore, the preferred tensile strength for the air impermeable material is within the range of 30-50 MPa. Suitable air impermeable polymeric materials can be obtained from Lubrizol Advanced Materials, Inc. as Estane® 58300 and 58315 materials. The phrase “air impermeable” indicates that the material resists flow of the inflation gas therethrough after final solidification of the coating materials, however, it does not require absolute impermeability. The air impermeable polymeric material and the adhesive material are preferably neither water-based nor solvent-based given their desired high molecular weights. Solubility of such materials is negligible and the materials are formed into a film type of coating by melting the materials and working with them as a liquid in an approximately 100 percent solids molten condition.

FIGS. 2-4 show a machine 51 used to make coated airbag 11. Machine 51 includes a coextruder 53 which has two extruder sections 55 with corresponding feed hoppers 57. Rotating screws 59 are located within each heated barrel 61. A pair of pipes or a manifold connects tips of both extruder barrels 61 to a combining block 63. Another pipe 65 or suitable conduit connects an end of combining block 63 to an elongated die 67. Die 67 has a laterally elongated exit slot downwardly facing toward fabric 14.

Fabric 14 is woven on jacquard loom 25 and then it is rolled up and transported to the coating line. It is then unrolled as it is fed into machine 51. Fabric 14 initially contacts against a lead-in roll 81. A pair of infrared heaters 83 and 85 preheat the adjacent outer surface of fabric 14 to a fabric temperature within the range of 100-180° C., and more preferably at about 150° C. The preheating advantageously delays solidification of the coating in order to allow deeper fabric penetration. Moreover, infrared heaters are ideally suited to allow tight packaging in their placement near coating die 67.

The hot fabric is then coated with the adhesive and air impermeable materials in a curtain-type coating 31 essentially along the full width of the fabric. The outer surface of fabric 14 is still hot, at a temperature of at least 100° C., where coating 31 is applied onto the fabric's outer surface, as this preheating will significantly improve adhesion and coverage of the coating. A dwell time between the fabric preheating step and the coating application is 10 seconds or less, and preferably 5 seconds or less, given the disclosed fabric travel speeds in the coating machine. Thus, downstream infrared heater 85 is 3 meters or less from coating die 67, and more preferably 1.5 meters or less, for 0.3 meters per second fabric speed. For faster fabric speeds, however, the heater to die distance can be greater (but with the same dwell time) as long as the fabric is sufficiently hot when the coating is applied.

Coating 31 is applied in a generally uniform thickness by die 67 onto fabric 14, exiting die 67 at about 20 thousandths of an inch thick while still molten. After contacting the surface of fabric 14 and subsequent solidification, the coating preferably has a total thickness within the range of about 1-6 thousandths of an inch and more preferably at about 2 thousandths of an inch, approximately half of which is the adhesive and half of which is the air impermeable material. The final solidified coverage of coating 31 onto fabric 14 is preferably within the range of 30-90 grams per square meter and more preferably at approximately 50 grams per square meter. The thermoplastic material is applied to the fabric at a temperature within the range of about 200-250° C. and preferably within the range of 204-216° C. Furthermore, fabric 14 is moving through machine 51 at about 0.3-1.6 meters per second and preferably 1 meter per second. Coating 31, however, is being extruded from die 67 onto fabric 14 at a slower speed, at approximately a 10:1 ratio of fabric-to-coating speed, therefore the fabric draws the coating in a thinning manner as it is being applied. Moreover, coating 31 is applied on the fabric such that the adhesive and air permeable materials preferably remain in two generally distinct layers, but with penetration of at least the adhesive into the outer fabric material.

A steel backing roll 87 controls the temperature of a contacting rubber covered roll 89. Fabric 14 is then pulled between rubber roll 89 and an adjacent chill roll 91. Chill roll 91 includes a set of closed loop, recirculating air/liquid cooling lines therein. Coating 31 remains molten when it and the fabric 14 are compressed between rolls 89 and 91. The elastomeric and cushioned rubber surface of roll 89 is compressible enough to absorb the thickness variations of the OPW weaving pattern of fabric 14 while maintaining the uniformity of the coating thickness against chill roll 91. Thus, this process is different than traditional calendaring. In other words, this combining station includes rubber roll 89 pressing against the backside of fabric 14 and the relatively large diameter steel, chill roll 91 that presses the molten coating 31 into the other fabric surface and cools the coating to solidify it. The two rolls are independently temperature controlled. Additionally, chill roll 91 imparts the mirror image of its own surface finish or texture into the coating surface (i.e., embossing) before the coating layers are cooled enough to be removed from the cooling roll surface.

Thereafter, the coated fabric moves around a stripper roll 93. The resulting one-side coated fabric is rolled up and then fed back into the beginning of machine 51 in an inverted manner, such that the opposite outside surface is upwardly facing for subsequent preheating, coating and solidification. The fully coated fabric is subsequently moved to a cutting station where each individual airbag is laser cut therefrom.

In greater detail, the process flow for the coextrusion coated fabric of the present application is performed in two simultaneous flows: one for the coating material and one for the fabric itself. The process flow of the coating material is further described as follows:

-   -   1. Plastic pellets of air impermeable TPU material 35 and         adhesive material 33 are pneumatically conveyed from shipping         containers to their respective feed hoppers 57 mounted above a         back of extruders 55.     -   2. Pellets are fed into the first flight of rotating screws 59         of extruders 55 which are tightly fitted in the heated steel         barrels 61.     -   3. The pellets are melted, deaerated and brought to a high         pressure by a progressive change in the pitch and depth of the         extruder flights of screws 59.     -   4. The resulting molten flow exits the tips of the extruders 55         at a rate that is precisely controlled by the speed of the         rotating extruder screws 59.     -   5. The above process is carried out simultaneously in two         extruders; one for adhesive layer 33 of coating 31 and one for         the outer exposed, air impermeable TPU layer 35 of the coating.     -   6. The flow from the two extruders 55 is fed to combining block         63 and then into extrusion die 67 that shapes the molten flow         into a wide, thin 2-layer curtain with the adhesive material on         one side of the curtain and the topcoat, air impermeable         material on the other side of the curtain.     -   7. Extrusion die 67 and its curtain of extrudate are positioned         immediately above the path of moving fabric 14 to allow the         application of a film of plastic coating 31 on the upward facing         surface of the moving fabric.

The previously disclosed example is employed for a side curtain airbag having an OPW fabric construction. Nevertheless, various features from the present application may be used with front or seat mounted airbags, cut and sew airbags, or even seat belt webbing, although many advantages of the present application may not be realized. Furthermore, it is alternately envisioned that the adhesive and air impermeable materials can be applied in a series rather than previously disclosed parallel manner by separate and spaced apart extrusion machines and dies, however, various advantages of the present application may not be achieved. Moreover, other heaters beyond infrared heaters, may alternately be employed, however, other heaters may be larger and have inferior performance. Additionally, certain aspects of the present application may be used without an adhesive layer if a suitable air impermeable material is otherwise used. While various materials, weaving patterns and exemplary characteristics have been disclosed, it should be appreciated that various other materials, patterns and characteristics can be employed. It is intended by the following claims to cover these and any other departures from the disclosed embodiments which fall within the true spirit of this invention. 

1. A method for making a vehicular airbag, the method comprising: (a) creating a one-piece woven airbag including a single fabric layer seam and a multiple fabric layer inflation chamber; (b) extruding a polymeric material; and (c) coating the extruded polymeric material upon the one-piece woven fabric, the coated polymeric material operably reducing air permeability through the fabric if the inflation chamber is inflated.
 2. The method of claim 1, further comprising preheating an outer surface of the fabric prior to the coating of the polymeric material, the heated surface of the fabric remaining hot during the coating.
 3. The method of claim 2, further comprising energizing an infrared heater to preheat the outer surface of the fabric within 10 seconds from where the coating is subsequently applied to the fabric.
 4. The method of claim 1, further comprising extruding an adhesive material and coating the adhesive material between the fabric and the polymeric material, such that the adhesive material is in direct contact with the fabric.
 5. The method of claim 4, wherein the polymeric material and the adhesive material are coextruded to a single die, and are subsequently and simultaneously coated onto the fabric in at least two substantially distinct layers.
 6. The method of claim 1, further comprising causing the entire solidified coating thickness for each outer surface of the fabric to have a thickness within the range of 1-6 thousandths of an inch and a coverage area within the range of about 30-90 grams per square meter.
 7. The method of claim 6, wherein the solidified coating includes the polymeric material and an adhesive material, each defining about half of the entire solidified coating thickness.
 8. The method of claim 1, wherein the polymeric material is a thermoplastic which is recyclable after solidifying.
 9. The method of claim 1, further comprising compressing the fabric and the molten coating material against a chill roll to cause penetration of the coated polymeric material into the fabric and to assist in solidifying the polymeric material.
 10. The method of claim 1, further comprising subsequently coating the opposite outside surface of the one-piece woven fabric after the polymeric material is coated and substantially solidified upon the initial outside surface of the one-piece woven fabric.
 11. The method of claim 1, further comprising applying the entire coating in a uniformly thick manner independent of thickness variations of the one-piece woven fabric.
 12. The method of claim 1, further comprising weaving a side curtain airbag from the fabric, wherein the airbag operably retains a majority of its inflation gas for at least five seconds after initial full inflation in order to assist with vehicular rollover protection.
 13. A method for making a vehicular fabric, the method comprising: (a) weaving the vehicular fabric using a one-piece woven fabric construction including weaving a single fabric layer seam to multiple overlapping fabric layers; (b) extruding an adhesive material; (c) extruding an air impermeable material; and (d) coating the extruded materials upon the fabric in a molten state; (e) wherein the fabric, adhesive material and air impermeable material are thermoplastics which are recyclable after solidifying.
 14. The method of claim 13, further comprising preheating an outer surface of the fabric prior to the coating of the air impermeable material, the heated surface of the fabric remaining hot during the coating.
 15. The method of claim 13, further comprising energizing an infrared heater to preheat an outer surface of the fabric within 10 seconds from where the coating is subsequently applied to the fabric.
 16. The method of claim 13, further comprising coextruding the air impermeable material and the adhesive material to a single die, and subsequently and simultaneously coating the materials onto the fabric in two substantially distinct layers.
 17. The method of claim 13, further comprising causing the entire solidified coating thickness for each outer surface of the fabric to have a thickness within the range of 1-6 thousandths of an inch and a coverage area within the range of about 30-90 grams per square meter.
 18. The method of claim 13, wherein the air impermeable material and the adhesive material each define about half of the entire solidified coating thickness.
 19. The method of claim 13, further comprising compressing the fabric and the molten materials against a chill roll to cause penetration of at least one of the coated materials into the fabric and to assist in solidifying the materials.
 20. The method of claim 13, further comprising subsequently coating the opposite outside surface of the fabric after the air impermeable material is coated and substantially solidified upon the initial outside surface of the fabric.
 21. The method of claim 13, further comprising applying the entire coating in a uniformly thick manner independent of thickness variations of the one-piece woven fabric.
 22. The method of claim 13, further comprising weaving a side airbag from the fabric, wherein the airbag operably retains a majority of its inflation gas for at least five seconds after initial full inflation in order to assist with vehicular rollover protection.
 23. A method of making an airbag, the method comprising: (a) making a side curtain airbag fabric; (b) applying an adhesive material onto the fabric; (c) applying a thermoplastic and leak-resistant material onto the fabric substantially simultaneously with the adhesive; and (d) emitting the materials in a molten and substantially insoluble state from at least one die onto the adjacent outer surface of the fabric in order to create a substantially uniformly applied thickness of the materials, substantially regardless of fabric thickness variations, and the total thickness of the materials on the outer surface of the fabric being within the range of 1-6 thousandths of an inch after they are solidified.
 24. The method of claim 23, further comprising preheating the outer surface of the fabric prior to the application of the leak-resistant material, the heated surface of the fabric remaining hot during the application.
 25. The method of claim 23, further comprising energizing an infrared heater to preheat the outer surface of the fabric within 10 seconds from where the leak-resistant material is subsequently applied to the fabric.
 26. The method of claim 23, wherein the leak-resistant material and the adhesive material are coextruded to a single die, and are subsequently and simultaneously coated onto the fabric in two substantially distinct layers.
 27. The method of claim 23, further comprising causing the entire solidified thickness of the materials having a coverage area within the range of about 30-90 grams per square meter.
 28. The method of claim 23, further comprising making the fabric as a one-piece woven construction including at least two multilayer portions connected by a single layer seam.
 29. The method of claim 23, further comprising compressing the fabric and at least one of the molten materials against a chill roll to cause penetration of at least one of the materials into the fabric and to assist in solidifying the materials.
 30. The method of claim 23, further comprising subsequently coating the opposite outside surface of the fabric after the leak-resistant material is coated and substantially solidified upon the initial outside surface of the fabric.
 31. The method of claim 23, further comprising applying the materials to the fabric in a continuously flowing curtain-like manner such that it is substantially uniformly thick independent of thickness variations of the fabric which is a one-piece woven fabric, the curtain-like application being uniformly coated along at least the majority width of the fabric.
 32. A method of making a vehicular airbag, the method comprising: (a) feeding vehicular airbag fabric into a coating machine; (b) heating an outside surface of the fabric to at least 100° C.; and (c) coating the heated fabric with an air impermeable material, after step (b), such that the outer surface of the fabric is still hot when coated.
 33. The method of claim 32, further comprising weaving a side curtain airbag from the fabric, wherein the airbag operably retains a majority of its inflation gas for at least five seconds after initial full inflation in order to assist with vehicular rollover protection.
 34. The method claim 33, further comprising: (a) creating the vehicular airbag fabric by weaving a one-piece woven airbag including a single fabric layer seam and a multiple fabric layer inflation chamber; (b) extruding the air impermeable material; and (c) coating an adhesive material between the one-piece woven fabric and the air impermeable material, the coated air impermeable material operably reducing air permeability through the fabric.
 35. The method claim 33, further comprising heating the surface of the fabric within the range of 100-180° C. within 10 seconds prior to the coating.
 36. The method claim 33, further comprising feeding the fabric through the coating machine at a speed within the range of 0.3-1.6 meters per second and applying the coating onto the fabric with a coverage area within about 30-90 grams per square meter.
 37. The method claim 33, further comprising heating the surface of the fabric to at least 150° C. within 5 seconds prior to the coating.
 38. The method claim 33, further comprising coating the fabric with a high molecular weight adhesive layer, and the air impermeable material being a high molecular weight thermoplastic polyurethane which is melted and applied in a substantially 100 percent solids, molten condition.
 39. A method of making a vehicular airbag, the method comprising: (a) making a one-piece woven airbag fabric having an integrally woven seam portion and a multiple layer inflation chamber portion; (b) heating the one-piece woven fabric to at least 100° C.; and (c) curtain coating a molten thermoplastic polymeric material and an adhesive material onto the one-piece woven fabric, after step (b), while a surface of the fabric still has a temperature of at least 100° C.
 40. The method claim 39, further comprising heating the surface of the fabric within the range of 100-180° C. within 10 seconds prior to the coating.
 41. The method claim 39, further comprising feeding the fabric through the coating machine at a speed within the range of 0.3-1.6 meters per second and applying the materials onto the fabric with a coverage area within about 30-90 grams per square meter.
 42. The method claim 39, further comprising heating the surface of the fabric to at least 150° C. within 5 seconds prior to the coating.
 43. The method claim 39, further comprising applying the materials in a substantially 100 percent solids and molten condition, the polymeric material including a high molecular weight thermoplastic polyurethane.
 44. A machine for coating a vehicular fabric, the machine comprising: a first extruder melting an air impermeable polymer; a second extruder melting an adhesive; at least one die operably coating the air impermeable polymer and adhesive onto the vehicular fabric as a continuous molten curtain of uniform thickness; and a heater operably preheating the vehicular fabric prior to coating, at a location within about 3 meters of the exit orifice of the die.
 45. The machine of claim 44, further comprising a chill roll and a compressible roll compressing the coated fabric therebetween while assisting in solidifying the coating on the fabric.
 46. The machine of claim 44, further comprising a lead-in roll located upstream of the die and chill roll, the heater further comprising at least two infrared heaters, at least one of the heaters being located upstream of the lead-in roll and at least the other of the heaters being located downstream of the lead-in roll.
 47. The machine of claim 44, further comprising a jacquard loom making a one-piece woven airbag fabric having a single layer seam woven to a multiple layer inflation chamber, and the machine applying the air impermeable polymer and the adhesive onto the one-piece woven airbag fabric with a solidified thickness within the range of 1-6 thousandths of an inch.
 48. A vehicular airbag comprising: a one-piece woven airbag fabric including a single layer seam woven to a multiple layer inflation chamber; a high molecular weight and substantially 100 percent solids adhesive located on outside surfaces of the one-piece woven fabric; and a high molecular weight and substantially 100 percent solids, thermoplastic polyurethane located on the adhesive; wherein the combined thermoplastic polyurethane and adhesive have a substantially uniform solidified thickness within the range of 1-6 thousandths of an inch and a coverage area on the one-piece woven fabric within the range of 30-90 grams per square meter.
 49. The airbag of claim 48, wherein the seam of the one-piece woven fabric includes at least two 3×3 woven baskets and at least two 2×2 woven baskets.
 50. The airbag of claim 48, wherein the thermoplastic polyurethane is polyether-based and has an ultimate elongation property of at least 300 percent.
 51. The airbag of claim 48, wherein the adhesive is an ethylene acrylate copolymer.
 52. The airbag of claim 48, wherein the thermoplastic polyurethane and the adhesive are olefinic.
 53. The airbag of claim 48, wherein the coated one-piece woven fabric is a side curtain airbag which operably retains inflation gas for at least five seconds from full initial inflation to assist rollover protection. 